A pulp mill is a manufacturing facility that converts wood chips or other plant fibre source into a thick fibre board which can be shipped to a paper mill for further processing. Pulp can be manufactured using mechanical, semi-chemical or fully chemical methods (kraft and sulfite processes). The finished product may be either bleached or non-bleached, depending on the customer requirements.
Wood and other plant materials used to make pulp contain three main components (apart from water): cellulose fibres (desired for papermaking), lignin (a three-dimensional polymer that binds the cellulose fibres together) and hemicelluloses, (shorter branched carbohydrate polymers). The aim of pulping is to break down the bulk structure of the fibre source, be it chips, stems or other plant parts, into the constituent fibres.
Chemical pulping achieves this by degrading the lignin and hemicellulose into small, water-soluble molecules which can be washed away from the cellulose fibers without depolymerizing the cellulose fibres (chemically depolymerizing the cellulose weakens the fibres). The various mechanical pulping methods, such as groundwood (GW) and refiner mechanical (RMP) pulping, physically tear the cellulose fibres one from another. Much of the lignin remains adhering to the fibres. Strength is impaired because the fibres may be cut. There are a number of related hybrid pulping methods that use a combination of chemical and thermal treatment to begin an abbreviated chemical pulping process, followed immediately by a mechanical treatment to separate the fibres. These hybrid methods include thermomechanical pulping (TMP) and chemithermomechanical pulping (CTMP). The chemical and thermal treatments reduce the amount of energy subsequently required by the mechanical treatment, and also reduce the amount of strength loss suffered by the fibres.
Contents |
Much of the information about the technology in following subsections is from the book by C.J. Biermann.[1]. The chemistry of the various pulping processes can be found in Sjöström's book.[2]
The most common fibre source for pulp mills is pulpwood. Other common sources are bagasse and fibre crops. The first step in all mills using wood (trees) as the fibre source is to remove the bark. Bark contains relatively few usable fibers and darkens the pulp. The removed bark is burned, along with other unusable plant material, to generate steam to run the mill. Almost all wood is then chipped before it processed further to free the fibers.
Removal of the bark is done in a barker (or debarker). The bark adhesion is about 3-5 kg/cm2 in the growing season (summer) and 2-3 times higher in the dormant season (winter). The bark of frozen logs is even more difficult to remove.
In chemical pulp mills the bark is introducing unwanted contaminants as calcium, silica and aluminum that are causing scaling and gives an extra load for the chemical recovery system. Birch bark contains betulin, a terpenoid that easily makes deposits in a pulp mill.
The earliest mills used sandstone grinding rollers to break up small wood logs called "bolts", but the use of natural stone ended in the 1940s with the introduction of manufactured stones with embedded silicon carbide or aluminum oxide. The pulp made by this process is known as "stone groundwood" pulp (SGW). If the wood is ground in a pressurized,sealed grinder the pulp is classified as "pressure groundwood" (PGW) pulp. Most modern mills use chips rather than logs and ridged metal discs called refiner plates instead of grindstones. If the chips are just ground up with the plates, the pulp is called "refiner mechanical" pulp (RMP), if the chips are steamed while being refined the pulp is called "thermomechanical" pulp (TMP). Steam treatment significantly reduces the total energy needed to make the pulp and decreases the damage (cutting) to fibers. Mechanical pulp mills use large amounts of energy, mostly electricity to power motors which turn the grinders. A rough estimate of the electrical energy needed is 10,000 megajoules (MJ) per tonne of pulp (2,750 kW·h per tonne)
Chemical pulping processes such as the kraft (or sulfate) process and the sulfite process remove much of the hemicelluloses and lignin. The kraft process does less damage to the cellulose fibers than the sulphite process, thereby producing stronger fibers, but the sulfite process makes pulp that is easier to bleach. The chemical pulping processes use a combination of high temperature and alkaline (kraft) or acidic (sulphite) chemicals to break the chemical bonds of the lignin.
The material fed into the digester must be small enough to allow the pulping liquor to penetrate the pieces completely. In the case of wood, the logs are chipped and the chips screened so that what is fed to the digester is a uniform size. The oversize chips are rechipped or used as fuel, sawdust is burned. The screened chips or cut plant material (bamboo, kenaf, etc.) goes to the digester where it is mixed an aqueous solution of the pulping chemicals, then heated with steam. In the kraft process the pulping chemicals are sodium hydroxide and sodium sulfide and the solution is known as white liquor. In the sulfite process the pulping chemical is a mixture of metal (sodium, magnesium, potassium or calcium) or ammonium sulfite or bisulfite.
After several hours in the digester, the chips or cut plant material breaks down into a thick porridge-like consistency and is "blown" or squeezed from the outlet of the digester through an airlock. The sudden change in pressure results in a rapid expansion of the fibers, separating the fibres even more. The resulting fiber suspension in water solution is called "brown stock".
Brown stock washers, using countercurrent flow, remove the spent cooking chemicals and degraded lignin and hemicellulose. The extracted liquid, known as black liquor in the kraft process, and red or brown liquor in the sulfite processes, is concentrated, burned and the sodium and sulfur compounds recycled in the recovery process. Lignosulfonates are a useful byproduct recovered from the spent liquor in the sulfite process.[3] The clean pulp (stock) can be bleached in the bleach plant or left unbleached, depending on the end use. The stock is sprayed onto the pulp machine wire, water drains off, more water is removed by pressing the sheet of fibers, and the sheet is then dried. At this point the sheets of pulp are several millimeters thick and have a coarse surface: it is not yet paper. The dried pulp is cut, stacked, bailed and shipped to another facility for whatever further process is needed.
Bleached kraft pulp and bleached sulfite pulp are used to make high quality, white printing paper. One of the most visible uses for unbleached kraft pulp is to make brown paper shopping bags and wrapping paper where strength is particularly important. A special grade of bleached sulfite pulp, known as dissolving pulp, is used to make cellulose derivatives such as methylcellulose which are used in a wide range of everyday products from laxatives to baked goods to wallpaper paste.
Some mills pretreat wood chips or other plant material like straw with sodium carbonate, sodium hydroxide, sodium sulfite, and other chemical prior to refining with equipment similar to a mechanical mill. The conditions of the chemical treatment are much less vigorous (lower temperature, shorter time, less extreme pH) than in a chemical pulping process, since the goal is to make the fibers easier to refine, not to remove lignin as in a fully chemical process. Pulps made using these hybrid processes are known as chemi-thermomechanical pulps (CTMP). Sometimes a CTMP mill is located on the same site as a kraft mill so that the effluent from the CTMP mill can be treated in the kraft recovery process to regenerate the inorganic pulping chemicals.
The United Nations Environmental Program (UNEP) has approved only two processes for making the chemical bleach chlorine dioxide, which produce 99.8% chlorine dioxide and contain only 0.2% elemental chlorine. Contamination of the chlorine dioxide with elemental chlorine is considered undesirable, and may lead to environmental pollution. While properly treated effluent may be safe to discharge into water catchment areas, mills which discharge untreated effluent pollute water ways with persistent organic pollutants (organochlorides and dioxins), and may breach the Stockholm Convention.